GLYCO® 393
Key Features
- Advanced machinable dry bearing material for high loads and precision requirements
- Thermoplastic based material for high load capacity and wear resistance under lubricated and non lubricated conditions.
- High PTFE content for significant friction reduction and for allowing use in unlubricated applications
- Best in class material in performance and enabling of multiple application cases (dry, greased, oiled, machining after assembly).
A high number of fluid lubricated applications need to be fit with self lubricating composite material bushings due to mixed friction conditions.
Increasing precision requirements (reduced misalignment or shaft clearance) needs to be achieved.
Increased specific loads are placed on the bearings.
GLYCO® 393 is a three layer composite material. A porous tin bronze sinter structure is applied on a steel back, which is impregnated with a PPS sliding material with friction improving and wear reducing additives. An overlay of the same sliding material is located above the filled bronze structure.
Surface roughness of Rz = 4 – 6 µm achievable through machining of the top layer with the proper process parameter (3000 – 5000 rpm, feed rate of 0,02 mm/rpm) and optimized tool.
Microsection
Microsection GLYCO® 393 according to ISO 3547 type P2
| 1 | PPS, PTFE and addtives |
| 2 | Tin bronze |
| 3 | Steel back |
| 4 | Tin layer (optional) |
Technical Data
| Properties | GLYCO® 393 |
|---|---|
| Material type | Thermoplastic based according to ISO 3547 type P2 |
| Composition | Steel back with sintered layer of tin bronze. Pore filling and cover layer (0.250 and 0.350 mm) of PPS, PTFE with additives, machineable |
| Application | Pumps, transmission, compressors, utility vehicles, etc. Other applications with risk of high bearing wear |
| Permissible stat. specific load | 250 MPa |
| Permissible dyn. specific load | 120 MPa |
| Maximum sliding velocity |
2 m/s (dry running) 2 m/s (greased) 10 m/s (oiled) |
| Operating temperature | -40 to 220 °C |
| Coefficient of friction | 0.03 to 0.10 (dry running and greased) |
| Stick-slip | negligible |
| Wear layer thickness (min.) | – |
| Lubrication
Friction Wear resistance Load capacity |
dry
+++ +++ +++
Grease
+++ +++ +++
Oil
+ +++ +++ |
| Ability to support edge loads (resulting from misalignment) | good |
| Ability to embed dirt and foreign particles | good |
| Ability to carry alternating loads | good |
| Ability to accommodate linear movement | good |
| Machining of sliding surface after mounting | line boring, turning |
| Technical sheet |
Available Designs
Materials of the
GLYCODUR® Portfolio
GLYCODUR® F / GLYCO® 92 – PTFE based according to ISO 3547 type P1
GLYCODUR ® F sliding bearings have a steel base, to which a 0.2 to 0.4 mm porous tin bronze layer is sintered.
[Learn more]GLYCODUR® A / GLYCO® 94 – Thermoplastic based according to ISO 3547 type P2
GLYCODUR® A dry sliding bearings have a steel base and a 0.2 to 0.4 mm sintered tin bronze layer.
[Learn more]GLYCO® 193 – Thermoplastic based according to ISO 3547 type P2
GLYCO® 193 is a three layer composite material. A porous tin bronze sinter structure is applied on a steel back.
[Learn more]All Materials of the
GLYCODUR® Portfolio
Catalogue program
- GLYCODUR® F
- Cylindrical bushings
- Flanged bushings
- Thrust Washers
- Strips
- GLYCODUR® A
- Cylindrical bushings
- Thrust Washers
- Strips