GLYCO® 97

Key Features

  • Maintenance-free operation lubrication for use under severe dry running conditions
  • High pv-value
  • Good wear resistance
  • High load capacity
  • Low friction
  • Rotating, oscillating and axial motion possible
  • Wide range of part design types

For some applications operated without any lubrication, maintenance free bearings do not achieve the targeted service life. Performances in friction improving the system efficiency are also below expectations.

Reasons could be the use of standard performance PTFE-materials, not optimized for dry running conditions at higher loads and long operation periods.

GLYCO® 97 is a three layer composite material. A porous tin bronze sinter structure is applied on a steel back. This layer is impregnated with a PTFE sliding material and a specific combination of fillers especially chosen to improve the performance of this material under dry running conditions. On the top of this filled bronze structure, a 5 to 30 μm thick overlay of the same sliding material is applied, providing the initial lubrication during the running-in of the application. 

GLYCO® 97 sliding bearings are therefore showing lower friction and in the same time higher wear resistance under dry operation compared to other standard PTFE-based materials. In addition, it is available on request with a thinner top layer offering advantages for applications involving a cataphoretic painting process.

Microsection

Microsection GLYCO®  97 according to ISO 3547 type P1

 

1PTFE, MoS2, BN with friction reducing additives
2Tin bronze
3Steel back
4Tin layer (optional)

 

Technical Data

PropertiesGLYCO® 97
Material typePTFE based according to ISO 3547 type P1
CompositionSteel back with sintered layer of tin bronze. Pore filling and cover layer (5 to 30 µm/0.0002 to 0.00118 in) of PTFE, MoS2, BN with friction reducing additives
ApplicationOptimised dry bearing material, good formability. Automotive dry running systems like vibration dampers, actuators, various hinges (door, trunk lid, hood, convertible roof), locking devices, pedal systems.
Permissible stat. specific load250 MPa
Permissible dyn. specific load100 MPa
Maximum sliding velocity 2 m/s (dry running)
Operating temperature-200 to 260 °C
Coefficient of friction0.09 to 0.20 (dry running)
Stick-slipnegligible
Wear layer thickness (min.)0.2 mm / 0.0079 in
Lubrication
Friction
Wear resistance
Load capacity
dry
++
++
++
Ability to support edge loads (resulting from misalignment)standard
Ability to embed dirt and foreign particlesstandard
Ability to carry alternating loadsgood
Ability to accommodate linear movementstandard
Machining of sliding surface after mountingcalibration